CAS No.: | 24968-12-5 |
---|---|
Formula: | (C12h12o4)N |
Material: | Polybutylene Terephthalate/PBT |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Color: | White |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Advantages |
1. Excellent transparency, outstanding resistance to aging. 2. It has good insulating properties and mechanical strength; to acid, alkali, salt has a strong resistance to corrosion; and because easy processing. |
Applications |
Minsheng supplies (brush bristles, elastic fiber, fluorescent tube, energy-saving bulb shell) |
Properties
|
Test Condition
|
Test Method
|
Unit
|
Typical Value
|
Physical
|
|
|
|
|
Specific Gravity
|
|
ISO1183-1-2012
|
g/cm³
|
1.64
|
Molding Shrinkage (Parallel)
|
|
ISO 294-4
|
%
|
0.4
|
Melt Flow Rate
|
250ºC/2.16kg
|
ISO1133:2011
|
g/10min
|
25
|
Mechanical
|
|
|
|
|
Tensile Stress at break
|
10mm/min
|
ISO 527-2
|
mpa
|
125
|
Tensile Strain at break
|
10mm/min
|
ISO 527-2
|
%
|
|
Flexural Strength
|
2mm/min
|
ISO 178:2010
|
mpa
|
210
|
Flexural Modulus
|
2mm/min
|
ISO 178:2010
|
mpa
|
9000
|
Charpy Impact
|
Notched, 23ºC
|
ISO 179
|
kj/m²
|
9
|
Charpy Impact
|
Unnotched, 23ºC
|
ISO 179
|
kj/m²
|
65
|
Thermal
|
|
|
|
|
Heat Deflection Temperature
|
1.80Mpa, 3.2mm, unannealed
|
ISO 75-1/-2
|
ºC
|
208
|
Heat Deflection Temperature
|
0.45Mpa, 3.2mm, unannealed
|
ISO 75-1/-2
|
ºC
|
220
|
Flammability
|
0.8-3.2mm
|
UL94
|
-
|
V-0
|
Glow-wire Ignition Temperature
|
|
|
ºC
|
IEC 60695
|
Electrical
|
|
|
|
|
Volume Resistivity
|
|
IEC 60093
|
Ω.cm
|
1.0×1016
|
Dielectric Strength, in oil
|
|
IEC 60243-1
|
KV/mm
|
20
|